PROPERTIES |
TEST METHODS |
UNIT |
VALUES |
Specific Gravity |
ASTM D-792 |
|
1.08 |
Heat Distortion Temperature |
ISO 75 |
|
70oC |
Vicat Softening Point at 10N |
ISO 306 |
|
105oC |
Notched Izod Impact @ 23oC |
ISO 180 |
KJ / m2 |
18 |
Melt Flow Index (230oC/ 5 kg) |
ISO 1133 |
g / 10 min |
2.2 |
Electronic Properties |
TEST METHODS |
UNITS |
PS-68067 |
Volume Resistivity |
IBI D007C |
Ω.cm |
4.57E+05 |
Volume Resistivity |
ASTM D4496 |
Ω.cm |
2.19E+08 |
Surface Resistivity |
ASTM D4496 |
glossy side |
Ω/sq |
6.05E+07 |
mat side |
8.15E+06 |
Surface Resistivity |
IBI D042 based on IEC167
and DIN53482 |
glossy side |
MD |
Ω/sq |
8.11E+06 |
TD |
2.88E+08 |
mat side |
MD |
3.45E+06 |
TD |
3.41E+05 |
Static Decay time (1000V) |
|
s |
immediate
discharge |
Tensile Modulus |
ISO 527/3 - ASTM D882 |
100 mm/min |
MD |
Mpa |
1330 |
TD |
1456 |
Tensile Strength at Yield |
ISO 527/3 - ASTM D882 |
100 mm/min |
MD |
Mpa |
28.0 |
TD |
25.4 |
Elongation at Break |
ISO 527/3 - ASTM D882 |
100 mm/min |
MD |
% |
69.2 |
TD |
36.1 |
|
材料寬度:12, 16, 24, 32, 44……符合EIA 481需求之寬度
材料厚度:0.3 – 2.0mm
|